| Density |
ISO 1183 |
0.960 |
g/cm³ |
| Melt Flow Rate at 190 °C and 5.0 kg |
ISO 1133 |
0.24 |
g/10 min |
| Tensile Strength at Yield |
ASTM D 638 @ Crosshead speed 50 mm/min |
24 |
MPa |
| Tensile Strength at Yield |
ISO 527 |
24 |
MPa |
| Tensile strength at Break |
ISO 527 |
> 30 |
MPa |
| Elongation at Break |
ISO 527 |
> 600 |
% |
| Flexural Modulus |
ASTM D 790 |
1,000 |
MPa |
| Carbon black dispersion |
ISO 18553 |
<3 |
Grading |
| Carbon black content |
ISO 6964 |
2.25 |
%wt |
| Oxidative induction time at 210°C |
ISO 11357 |
≥ 40 |
min |
| MRS classification |
ISO 12162/ISO 9080 |
10 |
MPa |
| Resistance to slow crack growth at 80°C |
ISO 13479 |
> 500 |
hrs |
| Rapid crack propagation Pc, S4 |
ISO 13477 |
> 10 |
bar |
| Resistance to gas constituents |
ISO 1167 |
> 20 |
hrs |