SCGC™ PP P842J is high flowability polypropylene impact copolymer designed for injection molding process. This resin is recommended for product that requires very high stiffness and very high processability.

Properties Test Methods Value Unit
Melt Flow Rate at 230 °C and 2.16 kg ASTM D 1238 40.00 g/10 min
Density ASTM D 1505 0.910 g/cm³
Melting Point ASTM D 2117 163 °C
HDT at 4.6 kg/cm² ASTM D 648 120 °C
Tensile Strength at Yield ASTM D 638 @ Crosshead speed 50 mm/min 295 kg/cm²
Tensile Strength at Break ASTM D 638 @ Crosshead speed 50 mm/min 180 MPa
Flexural Modulus ASTM D 790 14,500 kg/cm²
Izod Impact Strength at 23°C ASTM D 256 74 J/m
Izod Impact Strength at 0 °C ASTM D 256 49 J/m
Izod Impact Strength at -20 °C ASTM D 256 30 J/m
Rockwell Hardness ASTM D 785 80 R-Scale
Flammability UL-94 HB -